Improvement in the electrical properties of BCZT Ceramics induced by self‑seeds
บทคัดย่อ ( Abstract )
The powder was calcined at 1200 °C for 2 h and sintered at 1450 °C for 4 h. Phase formation and surface morphology were analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). Dielectric, piezoelectric and ferroelectric properties of the ceramics were investigated. The results indicated that all samples showed pure perovskite phase. Density and grain size values were in the range of 5.54–5.62 g/cm3 and 9.40–10.42 μm, respectively. Electrical properties changed with BCZT seed content. Samples with 3.0 mol% seed had the highest phase transition temperature (Tc), piezoelectric coefficient (d33) and thickness electromechanical coupling coefficient (kt) with values of 93 °C, 520 pC/N and 48%, respectively. Moreover, dielectric loss (tan δ) at room temperature was lower than 0.014 for all samples (at 1 kHz).
เอกสารวิจัย ( Paper )
ผู้เขียน ( Authors )
- ผิวพรรณ ประจันทร์ศรี
ข้อมูลการเผยแพร่ ( Journal Infomation )
ชื่อวารสารที่ตีพิมพ์
Applied Physics A
หน่วยงานเจ้าของวารสาร
Springer
ลิงค์ฐานข้อมูลวารสารที่เผยแพร่
http://scopus.com
ประเภทฐานข้อมูล
-
ประเมินบทความโดย
-
วันที่ได้รับการอนุมัติ
May 16, 2562
วันที่เผยแพร่
May 21, 2562
เผยแพร่ระดับ
ระดับนานาชาติ
เลขที่ ISBN / ISSN / DOI
-
ปีที่ - ฉบับที่ - หน้าที่
ปี 2019 ฉบับที่ 125 หน้าที่ 421
แหล่งทุนงานวิจัย
เงินจากแหล่งทุนอื่น ๆ
วันที่อัพเดตข้อมูลล่าสุด
2021-07-02 11:30:45